PENGARUH VARIASI WAKTU DAN BEDA TEGANGAN PADA PROSES ANODIZING TERHADAP KEKERASAN PERMUKAAN ALUMINIUM DAN KETEBALAN LAPISAN OKSIDA

Abstract

Aluminium seri 1100 merupakan material yang jarang dipakai untuk keperluan manufaktur di industri otomotif karena sifatnya yang lunak. Oleh karena itu, untuk menambah nilai fungsi dari aluminium seri 1100 agar bisa digunakan untuk bahan pembuatan velg racing, perlu adanya proses lagi setelah dibentuk, salah satunya dengan proses anodizing untuk memperbaiki sifat mekanis material. Dari permasalahan tersebut, penulis meneliti efek anodizing pada aluminium seri 1100 dengan variasi waktu yang digunakan 10 menit, 20 menit, dan 30 menit dengan tegangan 10 volt. Berdasarkan hasil variasi waktu terbaik kemudian di variasikan tegangan 10 volt, 20 volt, dan 30 volt. Hasil uji komposisi kimia spesimen menunjukkan bahwa kandungan aluminium 99,30% dan tergolong aluminium seri 1XXX. Nilai rata-rata kekerasan vickers tanpa anodizing sebesar 46,86 VHN. Nilai kekerasan vickers terbaik pada aluminium seri 1100 didapatkan dengan lama waktu anodizing 30 menit tegangan 10 volt dengan nilai rata-rata 68,21 VHN, dan nilai rata-rata kekerasan vickers optimum pada aluminium seri 1100 setelah di anodizing dengan tegangan listrik 20 volt selama 30 menit sebesar 76,86 VHN. Nilai terbaik ketebalan lapisan oksida pada aluminium seri 1100 setelah di anodizing selama 30 menit dengan tegangan 10 volt sebesar 76,48 µm, dan nilai tertinggi ketebalan lapisan oksida pada aluminium seri 1100 setelah di anodizing dengan tegangan 20 volt selama 30 menit sebesar 88,81 µm.

Kata kunci: aluminium, anodizing, kekerasan, ketebalan

Abstract

1100 series aluminum is rarely used for manufacture in automotive industry purposes because its soft. Therefore, to add the function scores of 1100 series aluminum which is used for material manufacture of racing wheels it is necessary to have another proces after being formed by anodizing process to repair the mechanical propeties of the material. According to the problems, the writer examined the effect of anodizing in 1100 series aluminum with used 10 minutes, 20 minutes, and 30 minutes variations of time with 10 volt voltage. Based on the results of the best time variations are varied with 10 volt, 20 volt, and 30 volt voltage. The specimens which is used are 1100 series aluminum. The result of chemical composition test, test specimen showed that aluminum matrix was 99,30% and classified as 1XXX series aluminum. The best score of vickers hardness in 1100 series aluminum were obtained 30 minute time anodizing with 10 volt voltage which have average score 68,21 VHN, and the best score average of vickers hardness in 1100 series aluminum after anodizing were 20 volt  electrical voltage with 30 minute time have score 76,86 VHN. The best score of oxide layer thickness in 1100 series aluminum after anodizing were 30 minute time anodizing with 10 volt voltage which have score 76,48 µm, and best score of oxide layer thickness in 1100 series aluminum after anodizing were 20 volt  voltage with 30 minute time have score 88,81 µm.

Keywords: aluminum, anodizing, hardness, thickness